Name: Bambu Lab Matt PLA Refill filament 1Kg (12 colors) - Refill
Brand: Bambu Lab
SKU: 6457
Price: 29.99 EUR
Availability: InStock

description

Technical specification

Contents of order

Documentation

Notice

Filament PLA Matt Refill Bambu Lab

Discover Bambu Lab's Matt Refill PLA filament, a must-have for 3D printing enthusiasts looking for a flawless matte finish. This top-quality filament is specially designed to give 3D prints an elegant matt finish, adding a unique touch to your creations.

RFID for intelligent printing

All the printing parameters are integrated into the RFID, which can be read via our AMS (Automatic Material System).

Load and print! No more tedious set-up steps.

Print your own reel now

The Bambu Lab 3D printer comes with a spool model. Print Spool Part 1&2 from the built-in files!

If you do not have the reel model in your printer, please click here to download.

Instructions for the printed reel


When you have finished printing, you will have a wide part (1x), a narrow part (1x) and a spacer (2x).		Find the locator (a small block on the wide part). Align it with the notch on the inner ring of the filament roll. Insert the wide part into the filament roll.

Step 1. Insert the narrow piece and align the groove of each piece inside the spool until it is firmly pressed into the wide piece. Step 2. Once firmly seated in the wide piece, rotate the narrow piece clockwise until it slides into place and you hear it lock.		Step 1. Make sure the spacer is installed inside the coil (under the triangle). Step 2. Tear and remove the plastic strips.

Installing the filament in the spool

description

Technical specification

Contents of order

Documentation

Notice

Properties	Data
Drying parameters before printing	55 °C, 8 h
Printing and maintaining container humidity	< 20% RH (sealed, with desiccant)
Nozzle temperature	190 - 230 °C
Bed temperature (with PVP adhesive)	35 - 45 °C
Print speed	< 300 mm/s
Density	1.31 g/cm³
Softening temperature Vicar	63 °C
Thermal deviation temperature	58 °C
Melting temperature	163 °C
Melting index	39.4 +/- 3.2 g/10 min
Tensile strength	32 +/- 3 MPa
Elongation at break	32.8 +/- 4.3 %
Flexural modulus	2360 +/- 250 MPa
Flexural strength	53 +/- 2 MPa
Shock resistance	19.2 +/- 3.7 kJ/m²