« Back to the category
» 3D FILAMENTS

Bambu Lab PLA-CF filament 1Kg (7 colors)

Bambu Lab PLA-CF filament 1Kg (7 colors)
See larger image
Bambu Lab PLA-CF filament 1Kg (7 colors)
Bambu Lab PLA-CF filament 1Kg (7 colors)
Bambu Lab PLA-CF filament 1Kg (7 colors)
Bambu Lab PLA-CF filament 1Kg (7 colors)
Bambu Lab PLA-CF filament 1Kg (7 colors)
Bambu Lab PLA-CF filament 1Kg (7 colors)
Bambu Lab PLA-CF filament 1Kg (7 colors)

42.96€ Incl Tax

Available Product available

Spool included
Dry out before use
AMS compatible
1.75 mm / 1kg

Colors *

Weight *

Please fill all required fields
Quantity : 
+
-

Add to cart
Request a quotation

description
Technical specification
Contents of order
Documentation
Notice

 

 

Filament PLA-CF Bambu Lab

 

Bambu PLA-CF is carbon fiber reinforced PLA with improved stiffness and strength. PLA-CF is easy to print and beginner-friendly like regular PLA. It is AMS compatible with low clogging risk at high-speed printing. The prints are in matte finish with almost invisible layer lines, which make it suitable for printing general engineering parts or models requiring a better appearance, like bike frames, brackets and toys.

 

 

 

 

 

Carbon fiber texture & Minimized layer lines

 

The addition of carbon fiber gives prints a unique matte finish and effectively hides layer lines, providing a smooth, premium look.

 

 

 

 

 

 

 

Display of Prints

 

Bambu PLA-CF could be paired with any PLA series filament to make your prints more colorful and achieve various texture requirements.

 

 

 

 

 

Improved mechanical properties

Bambu PLA-CF exceeds the mechanical properties of PLA Matte in XY Bending Strength, Z Bending Strength, XY Bending Modulus, Z Bending Modulus, XY Impact Strength, and Z Impact Strength by between 20% and 115%, making it more suitable for printing models with higher strength requirements.

 

 

 

 

 

Mechanical Properties Comparison

 

 

 

 

 

Stablized printing dimension

 

Bambu PLA-CF features low shrinkage and warping resistance to achieve a perfect matching accuracy between prints parts.

 

 

 

 

Minimal effort in support removal

 

Bambu PLA-CF is designed to support itself. It can be removed more easily compared to regular PLA, and still maintains a smooth support surface.

 

 

 

 

 

 

Not prone to clogging in high-speed printing

 

Bambu PLA-CF is just as easy to print as regular PLA. It can be printed smoothly and consistently at high speed without clogging.

 

 

 

 

 

 

RFID for Intelligent Printing

 

All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).

Load and print! No more tedious setting steps.

 

 

 

 

 

Back to top
description
Technical specification
Contents of order
Documentation
Notice

 

 

PropertiesData
Drying parameters before printing55 °C, 8 h

Printing and maintaining container humidity

< 20% RH (sealed, with desiccant)
Nozzle temperature210 - 240 °C
Bed temperature (with PVP adhesive)35 - 45 °C
Print speed< 200 mm/s
Density1.22 g/cm³
Softening temperature Vicar69 °C
Thermal deviation temperature55 °C
Melting temperature165 °C
Melting index3.7 +/-  0.6 g/10 min
Tensile strength38 +/-  4 MPa
Elongation at break12.7 +/-  3.4 %
Flexural modulus3700 +/- 220 MPa
Flexural strength96 +/-  3 MPa
Shock resistance23.2 +/-  3.7 kJ/m²

 

 

 

Back to top
description
Technical specification
Contents of order
Documentation
Notice

 

 

     • 1 spool of Bambu Lab PLA-CF filament 1,75mm 1Kg  

 

     • Instructions and spool sticker

 

 

 

Back to top
description
Technical specification
Contents of order
Documentation
Notice

 

 

Filament Guide (EN)

 

Technical Data Sheet (EN)

 

Safety Data Sheet (EN)

 

 

 

Back to top
description
Technical specification
Contents of order
Documentation
Notice
Back to top
In the same category
Customers have also purchased
Products viewed
< >
Back to top
In the same category
Customers have also purchased
Products viewed
< >
Back to top
In the same category
Customers have also purchased
Products viewed
< >
Back to top
The administrator of the site is online now! Talk - ask your questions to webmaster