Bambu Lab PAHT-CF filament (500g or 1Kg)

Bambu Lab PAHT-CF filament (500g or 1Kg)
See larger image
53.94€ Incl Tax

Available Product available

With Spool
Dry out before use
AMS compatible
500g or 1Kg

Weight *

Please fill all required fields
Quantity : 
+
-

Add to cart
Request a quotation

description
Technical Data Sheet
Contents of order
Documentation
Notice

 

 

Filament PAHT-CF Bambu Lab

 

Bambu PAHT-CF is a composite of PA12 and carbon fiber. Inheriting the advantages of low water absorption from PA12 and high-performance carbon fiber, Bambu PAHT-CF offers excellent mechanical and thermal properties that can be maintained well even when the prints get wet. Higher Z adhesion layers and flexibility make it ideal for creating engineering parts such as functional prototypes, machining fixtures, injection molds, jigs, and low-volume production parts.

 

 

 

 

Low water absorption

 

With a 50% lower water absorption rate compared to normal PA-CF,

Bambu PAHT-CF maintains excellent mechanical properties and dimensional stability even when exposed to high humidity.

 

 

 

 

 

Deflection from Dry to Wet

 

 

 

 

 

 

 

Mechanical Properties Comparison

 

 

Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.

 

 

 

 

 

Exceptional Z-bonding

Bambu PAHT-CF shows much higher adhesion in Z layers compared to normal PA-CF,

bringing it the ability to withstand high levels of impact or stress without breaking or deforming.

 

 

 

 

 

 

 

 

 

 

Z-layer Performance

 

 

 

 

 

 

 

 

High tensile strength

 

Bambu PAHT-CF is designed to meet the demands of various industrial

and engineering applications where high strength and durability are required.

 

 

 

 

Designed for high-temperature resistance

 

The heat deflection temperature of Bambu PAHT-CF is up to 194℃ (0.45MPa)*, making it useful in applications where the printed parts may be exposed to high temperatures without deforming or losing their strength.

 

*The long-term temperature resistance is related to the structure and usage scenario of the model itself.

 

 

 

 

 

 

Reusable spool

 

 

Bambu PAHT-CF comes with a high-temperature resistant spool, which is not prone to deformation in the drying process. Continuing our concept of reducing plastic waste, the spool can also be reused with other Bambu refills.

 

 

 

 

 

 

 

 

RFID pour l'impression intelligente

 

 

Tous les paramètres d'impression sont intégrés dans la RFID, qui peut être lue via notre AMS (Automatic Material System).

Chargez et imprimez ! Plus d'étapes de réglage fastidieuses.

 

 

 

 

 

 

 

 

Back to top
description
Technical Data Sheet
Contents of order
Documentation
Notice

 

 

PropertiesData
Drying parameters before printing80 °C, 8 - 12 h

Printing and maintaining container humidity

< 20% RH (sealed, with desiccant)
Nozzle temperature260 - 290 °C
Bed temperature (with PVP adhesive)80 - 100 °C
Print speed< 100 mm/s
Density1.06 g/cm³
Softening temperature Vicar220 °C
Thermal deviation temperature194 °C
Melting temperature225 °C
Melting index14.4 +/- 2.0 g/10 min
Tensile strength88 +/- 7 MPa
Elongation at break10.4 +/- 0.7 %
Flexural modulus4120 +/- 290 MPa
Flexural strength140 +/- 8 MPa
Shock resistance57.5 +/- 3.4 kJ/m²

 

 

 

Back to top
description
Technical Data Sheet
Contents of order
Documentation
Notice

 

 

     • 1 Spool of Bambu Lab PAHT-CF filament 1,75mm 1Kg  / 0,5Kg

 

     • Instructions and spool sticker

 

 

 

Back to top
description
Technical Data Sheet
Contents of order
Documentation
Notice

 

 

Filament Guide (EN)

 

Technical Data Sheet (EN)

 

Safety Data Sheet (EN)

 

 

 

Back to top
description
Technical Data Sheet
Contents of order
Documentation
Notice
Back to top
In the same category
Customers have also purchased
Products viewed
< >
Back to top
In the same category
Customers have also purchased
Products viewed
< >
Back to top
In the same category
Customers have also purchased
Products viewed
< >
Back to top
The administrator of the site is online now! Talk - ask your questions to webmaster